Fatigue strength improvement of an aluminum alloy with a cracklike surface defect using shot peening and cavitation peening

(چکیده مقاله) :
Abstract :

The effects of shot peening (SP) and cavitation peening (CP) on the bending fatigue strength of the 7075 aluminum alloy with a crack-like surface defect were investigated. Test specimens containing a small semicircular slit were subjected to SP and CP. Bending fatigue tests were conducted on the specimens to determine the fatigue strength and critical depth (ac) of the semicircular slit that can be rendered harmless by peening. The results indicated that fatigue strengths increased by peening and that semicircular slits less than 0.1 and 0.2mm in depth were rendered harmless by SP and CP, respectively. The ac values estimated based on fracture mechanics were similar to experimental values, indicating that ac was affected by the distribution of the compressive residual stress induced by peening.

(توضیحات تکمیلی) :

(توضیحات تکمیلی) :
Description :

مقاله ISI انگلیسی اصلی
سال انتشار:2018
فایل ISI انگلیسی اصلی ، با فرمت Pdf
تعداد صفحات فایل ISI انگلیسی اصلی: 11 صفحه
جهت دسترسی به ترجمه این مقاله به صفحه قبل بازگردید مقاله ای که در سمت چپ ، این مقاله قرار دارد ترجمه این مقاله می باشد .

Authors / Descriptions(نویسندگان/توضیحات): نویسندگان / توضیحات: مقاله ISI مربوط به ترجمه مقابل / ارتقاء مقاومت خستگی یک آلیاژ آلومینیم با نقص ترک مانند با استفاده از ساچمه کوبی و حفره کوبی / نویسندگان: Koji Takahashia,⁎, Hiroko Osedoa, Takaya Suzukia, Shinsaku Fukudab
Sent date(تاریخ ارسال) : 1398/03/24  |   6/14/2019
Number of visits(تعداد بازدید): 650
Key words (کلمات کلیدی): Cavitation peening; Shot peening; Fatigue strength; Surface defect; Aluminum alloy
Number of pages(تعداد صفحات) : 11
نظرات کاربران در مورد این آگهی
در حال حاضر هیچ نظری ثبت نگردیده است .
ارسال پیام

مقالات مرتبط